The advancement of nanobiocomposites reinforced with 2D nano-materials plays a pivotal role in enhancing bone tissue engineering. In this study, we introduce a nanobiocomposite that reinforces bovine collagen with 2D nano-talc, a recently exfoliated nano-mineral. These nanobiocomposites were prepared by blending collagen with varying concentrations of 2D nano-talc, encompassing mono- and few-layers talc from soapstone nanomaterial. Extensive characterization techniques including AFM, XPS, nano-FTIR, s-SNOM nanoimaging, Force Spectroscopy, and PeakForce QNM® were employed. The incorporation of 2D nano-talc significantly enhanced the mechanical properties of the nanobiocomposites, resulting in increased stiffness compared to pristine collagen. In vitro studies supported the growth and proliferation of osteoblasts onto 2D nano-talc-reinforced nanobiocomposites, as well as showed the highest mineralization potential. These findings highlight the substantial potential of the developed nanobiocomposite as a scaffold material for bone tissue engineering applications.

The role of defects in two-dimensional semiconductors and how they affect the intrinsic properties of these materials have been a widely researched topic over the past few decades. Optical characterization techniques such as photoluminescence and Raman spectroscopies are important tools to probe the physical properties of semiconductors and the impact of defects. However, confocal optical techniques present a spatial resolution limitation lying in a μm-scale, which can be overcome by the use of near-field optical measurements. Here, we use tip-enhanced photoluminescence and Raman spectroscopies to unveil the nanoscale optical properties of grown MoS2 monolayers, revealing that the impact of doping and strain can be disentangled by the combination of both techniques. A noticeable enhancement of the exciton peak intensity corresponding to trion emission quenching is observed at narrow regions down to a width of 47 nm at grain boundaries related to doping effects. Besides, localized strain fields inside the sample lead to non-uniformities in the intensity and energy position of photoluminescence peaks. Finally, two distinct MoS2 samples present different nano-optical responses at their edges associated with opposite strains. The edge of the first sample shows a photoluminescence intensity enhancement and energy blueshift corresponding to a frequency blueshift for E2g and 2LA Raman modes. In contrast, the other sample displays a photoluminescence energy redshift and frequency red shifts for E2g and 2LA Raman modes at their edges. Our work highlights the potential of combining tip-enhanced photoluminescence and Raman spectroscopies to probe localized strain fields and doping effects related to defects in two-dimensional materials.